Product Details
Place of Origin: China
Brand Name: LHTi
Certification: ISO9001:2015; TUV; SGS;BV
Model Number: Titanium Sheet
Payment & Shipping Terms
Minimum Order Quantity: 50 kg
Packaging Details: Plywood box with soft foam for additional protection
Delivery Time: 10-28 work days
Payment Terms: T/T, MoneyGram, L/C, Western Union
Supply Ability: 200000 kg per month
Standard: |
ASTM B265 |
Technology: |
Cold Rolled |
Shape: |
Square |
Surface: |
Polished, Acid Washing |
Standard: |
ASTM B265 |
Technology: |
Cold Rolled |
Shape: |
Square |
Surface: |
Polished, Acid Washing |
Gr9 Gr12 Thin Titanium Sheet Acid Washing
Appearance: Silver grey white metal
Melting point: 194k (1668°C, 3034°F)
Boiling point: 3560 K (3287°C, 5949°F)
Density (near room temperature) : 4.506 g/cm3
Liquid time (melting point) : 4.11 g/cm3
Heat of fusion: 14.15 kJ/mol
Heat of vaporization: 425 kJ/mol
Molar heat capacity: 25.060 J/(mol·K)
Gr12 Ti-0.3Mo-0.8Ni titanium molybdenum nickel alloy plate is a kind of corrosion resistance titanium alloy, is in order to improve the pure titanium gap corrosion performance of the alloy, the alloy contains 0.3%Mo and 0.8%Ni, not only strengthen the alloy, but also for high temperature, low PH fireworks without or weak reducing acid has good gap corrosion resistance, Its corrosion resistance is significantly better than pure titanium plate. It also has good process plasticity and welding performance and has been widely used in chemical industry.
| Chemical requirements | |||||||||||
| N | C | H | Fe | O | Al | V | Pd | Mo | Ni | Ti | |
| Gr1 | 0.03 | 0.08 | 0.015 | 0.20 | 0.18 | / | / | / | / | / | bal |
| Gr2 | 0.03 | 0.08 | 0.015 | 0.30 | 0.25 | / | / | / | / | / | bal |
| Gr5 | 0.05 | 0.08 | 0.015 | 0.40 | 0.20 | 5.5~6.75 | 3.5~4.5 | / | / | / | bal |
| Gr7 | 0.03 | 0.08 | 0.015 | 0.30 | 0.25 | / | / | 0.12~0.25 | / | / | bal |
| Gr12 | 0.03 | 0.08 | 0.015 | 0.30 | 0.25 | / | / | / | 0.2~0.4 | 0.6~0.9 | bal |
| Tensile requirements | |||||
| Grade | Tensile srength(min) | Yeild strength(mm) | Elongation(%) | ||
| KSI | MPa | Ksi | MPa | ||
| 1 | 35 | 240 | 20 | 138 | 24 |
| 2 | 50 | 345 | 40 | 275 | 20 |
| 5 | 130 | 895 | 120 | 828 | 10 |
| 7 | 50 | 345 | 40 | 275 | 20 |
| 12 | 70 | 438 | 50 | 345 | 18 |