Home > products > Titanium Rod > TA18 Gr9 3al2.5v Titanium Bar ASTM F67 Non Magnetic Sandblasting

TA18 Gr9 3al2.5v Titanium Bar ASTM F67 Non Magnetic Sandblasting

Product Details

Place of Origin: China baoji

Brand Name: LHTi

Certification: ISO9001:2015

Model Number: Ti bar

Payment & Shipping Terms

Minimum Order Quantity: 50kg

Packaging Details: Wooden case or as per client requirement

Delivery Time: 10-15days

Payment Terms: L/C, D/A, T/T, Western Union

Supply Ability: 10000 Piece/Pieces per Month

Get Best Price
Highlight:

3al2.5v Titanium Bar

,

Gr9 Titanium Bar

,

ASTM F67 Titanium Bar

Grade:
Gr9 3al2.5v
Material:
Pure Titanium And Titanium Alloys
Application:
Industrial, Industry/medical
Length:
<12000mm
Shape:
Round
Technique:
Forged
Weight:
As Length
Processing Service:
Cutting
Standard:
ASTM B348/ASTM F67/ASTM F136
Surface Treatment:
Polished,Acid Wash,Sand Blast
Key Word:
Titanium Rod
Grade:
Gr9 3al2.5v
Material:
Pure Titanium And Titanium Alloys
Application:
Industrial, Industry/medical
Length:
<12000mm
Shape:
Round
Technique:
Forged
Weight:
As Length
Processing Service:
Cutting
Standard:
ASTM B348/ASTM F67/ASTM F136
Surface Treatment:
Polished,Acid Wash,Sand Blast
Key Word:
Titanium Rod
TA18 Gr9 3al2.5v Titanium Bar ASTM F67 Non Magnetic Sandblasting

TA18 Ti 3Al2.5V Alloy Grade 9 Titanium Bar

 

TA18 titanium alloy is an advanced α-type titanium alloy with a nominal composition of Ti-3A12V. It was developed as a cold processable pipe material. At room temperature and high

At temperature, its strength is 209% -50% higher than pure titanium, and its welding performance and cold forming performance are better than TC4 alloy. The maximum operating temperature is about 315 ° C. Although the strength of this alloy is not as high as that of TC4 alloy, it has been widely used because of its excellent cold workability.

 

Product Description

Product name

TA18 Ti 3Al2.5V Alloy Grade 9 Titanium Bar

Standard ASTMB348/ASTM F67/ASTM F136
Material Pure titanium and titanium alloys
Advantages

1. Resistance to acid and alkali corrosion, seawater corrosion and sewage corrosion

2. Low density, light weight

3. The non-magnetic

4. When used between -253-600°, its tensile strength is almost the highest among metals

 

Chemical compositions(weight%,<=)
Main component other
Ti V Fe C N H O single total
Remain 1.5-3.0 0.25 0.08 0.05 0.015 0.12 0.10 0.30

 

Physical properties(>=)
alloy composition

Σb

Tensile Strength

(Mpa)

σr0.2

Yield Strength

(Mpa)

 

ψ

Elongation

(%)

Ti 3Al2.5V Ksi Mpa Ksi Mpa 15F
90 620 1010 13

 

TA18 Gr9 3al2.5v Titanium Bar ASTM F67 Non Magnetic Sandblasting 0

 

TA18 Gr9 3al2.5v Titanium Bar ASTM F67 Non Magnetic Sandblasting 1

TA18 Gr9 3al2.5v Titanium Bar ASTM F67 Non Magnetic Sandblasting 2

Chemical Composition
Grade
N
C
H
Fe
O
Al
V
Pa
Ti
Gr1
0.03
0.08
0.015
0.2
0.18
/
/
/
Remain
Gr2
0.03
0.08

 0.015

0.3
0.25
/
/
/
Remain
Gr5
0.05
0.08
0.015
0.4
0.2
5.5~6.75
3.5~4.5
/
Remain
Gr7
0.03
0.08
0.015
0.3
0.25
/
/
0.12~0.25
Remain
Gr9
0.03
0.08
0.015
0.25
0.15
2.5~3.5
2.0~3.0
/
Remain
Mechanical Property
Material &grade
Yield strength(MPa)min
Tensile strength (Mpa)
Elongation (%)
GR1
240
170-310
24
GR2
345
275-450
20
GR3
450
380-550
18
GR4
550
483-655
15
GR5
895
830
10
GR7
345
485
15
GR9
860
725
10
GR12
483
345
18

 

Professional manufacturer supply ASTM B 338 Gr2 OD25*WT1.5 titanium seamless pipe

TA18 Gr9 3al2.5v Titanium Bar ASTM F67 Non Magnetic Sandblasting 4TA18 Gr9 3al2.5v Titanium Bar ASTM F67 Non Magnetic Sandblasting 5